TECHNICAL DETAILS

SUMMARY OF THE MAIN ASTM STANDARDS GENERALLY USED FOR PIPING

ASTM

Grade

Chemical Requirements Percent (%)

Mechanical Requirements

C

max

Mn

Max

P

Max

S

Max

Si

Max

Ni

Cr.

Mo

Cu

Others

Tensile Strength

Mini-MPa/Psi

Yield Strength

Mini-MPa/Psi

Elong mini

%

Impact test at

C

F

A 53

Types A

0.25

0.95

0.05

0.06

 

0.40 max

0.40 max

0.15 max

0.40 max

0.08 max

330-48000

205-30000

36

 

 

B

0.30

1.20

0.05

0.06

 

0.40 max

0.40 max

0.15 max

0.40 max

0.08 max

415-60000

240-35000

29.5

 

 

A 106

A

0.25

0.27-0.93

0.035

0.025

0.10 mini

0.40 max

0.40 max

0.15 max

0.40 max

0.08 max

330-48000

205-30000

L35-T25

 

 

B

0.30

0.29-1.06

0.035

0.025

0.10 mini

0.40 max

0.40 max

0.15 max

0.40 max

0.08 max

415-60000

240-35000

L30-T16.5

 

 

C

0.35

0.29-1.06

0.035

0.025

0.10 mini

0.40 max

0.40 max

0.15 max

0.40 max

0.08 max

485-70000

275-40000

L30-T16.5

 

 

A 312

TP 304

0.08

2.00

0.040

0.030

0.75

8.00-11.0

18.0-20.0

 

 

 

515-75000

205-30000

L35-T25

 

 

TP 304L

0.035

2.00

0.040

0.030

0.75

8.00-13.0

18.0-20.0

 

 

 

485-70000

170-25000

L35-T25

 

 

TP 310S

0.08

2.00

0.045

0.030

0.75

19.0-22.0

24.0-26.0

0.75 max

 

 

515-75000

205-30000

L35-T25

 

 

TP 316

0.08

2.00

0.040

0.030

0.75

11.0-14.0

16.0-18.0

2.00-3.00

 

 

515-75000

205-30000

L35-T25

 

 

TP 316L

0.035

2.00

0.040

0.030

0.75

10.0-15.0

16.0-18.0

2.00-3.00

 

 

485-70000

170-25000

L35-T25

 

 

TP 317L

0.035

2.00

0.040

0.030

0.75

11.0-15.0

18.0-20.0

3.00-4.00

 

 

515-75000

205-30000

L35-T25

 

 

TP 321

0.08

2.00

0.040

0.030

0.75

9.00-13.0

17.0-20.0

 

 

5C<Ti0.70%

515-75000

205-30000

L35-T25

 

 

TP 347

0.08

2.00

0.040

0.030

0.75

9.00-13.0

17.0-20.0

 

 

10C<Cb+Ta<1.00%

515-75000

205-30000

L35-T25

 

 

A 333

3

0.19

0.31-0.64

0.025

0.025

0.18-0.37

3.18-3.82

 

 

 

 

450-65000

205-35000

L30-T20

-100

-150

4

0.12

0.50-1.05

0.025

0.025

0.18-0.37

0.47-0.98

0.44-1.01

 

0.40-0.75

Ai:0.40-0.30%

415-60000

240-35000

L30-T16.5

-100

-150

6

0.30

0.29-1.06

0.025

0.025

0.10 mini

 

 

 

 

 

415-60000

240-35000

L30-T16.5

-45

-50

7

0.19

0.90

0.025

0.025

0.13-0.32

2.03-2.57

 

 

 

 

450-65000

240-35000

L30-T22

-75

-100

8

0.13

0.90

0.025

0.025

0.13-0.32

8.40-9.60

 

 

 

 

690-100000

515-75000

L22

-195

-320

9

0.20

0.40-1.06

0.025

0.025

 

1.60-2.24

 

 

0.75-1.25

 

435-63000

315-46000

L28

-75

-100

A 335

P1

0.10-0.20

0.30-0.80

0.025

0.025

0.50

 

 

0.44-0.65

 

 

380-55000

205-30000

L30-T20

 

 

P2

0.10-0.20

0.30-0.61

0.025

0.025

0.10-0.30

 

0.50-0.81

0.44-0.65

 

 

380-55000

205-30000

L30-T20

 

 

P5

0.15

0.30-0.60

0.025

0.025

0.50

 

4.00-6.00

0.45-0.65

 

 

415-60000

205-30000

L30-T20

 

 

P9

0.15

0.30-0.60

0.025

0.025

0.25-1.00

 

8.00-10.0

0.90-1.10

 

 

415-60000

205-30000

L30-T20

 

 

P11

0.15

0.30-0.60

0.025

0.025

0.50-1.00

 

1.00-1.50

0.44-0.65

 

 

415-60000

205-30000

L30-T20

 

 

P12

0.15

0.30-0.61

0.025

0.025

0.50

 

0.80-1.25

0.44-0.65

 

 

415-60000

205-30000

L30-T20

 

 

P15

0.05-0.15

0.30-0.60

 

 

1.15-1.65

 

 

0.44-0.65

 

 

415-60000

205-30000

L30-T20

 

 

P21

0.15

0.30-0.60

0.025

0.025

0.50

 

2.65-3.35

0.80-1.06

 

 

415-60000

205-30000

L30-T20

 

 

P22

0.15

0.30-0.60

0.025

0.025

0.50

 

1.90-2.60

0.87-1.13

 

 

415-60000

205-30000

L30-T20

 

 

P91

0.08-0.12

0.30-0.60

0.020

0.010

0.20-0.50

0.40 max

8.00-9.50

0.85-1.05

 

N0.30-0.70%Ai0

.04%max//0.06-0.10

0.18-0.25

585-85000

415-65000

L20

 

 

A 358

TP 304

0.08

2.00

0.045

0.030

0.75

8.0-10.50

18.0-20.0

-

 

 

Class 1 :  Double welded pipes & full Radiography

Class 2 :  Double welded no Radiography

Class 3 :  Single welded full Radiography

Class 4 :  Single welded full Radiography root pass

                 without addition of filler metal

Class 5 :  Double Welded sport Radiography

TP 310S

0.08

2.00

0.045

0.030

0.75

19.0-22.0

24.0-26.0

-

 

 

TP 316

0.08

2.00

0.045

0.030

0.75

10.0-14.0

16.0-18.0

2.0-3.0

 

 

TP 316L

0.030

2.00

0.045

0.030

0.75

10.4-14.0

16.0-18.0

2.0-3.0

 

 

TP 317L

0.035

2.00

0.045

0.030

0.75

11.0-15.0

18.0-20.0

3.0-4.0

 

 

TP 321

0.08

2.00

0.045

0.030

0.75

9.0-12.0

17.0-19.0

-

 

N0.10 max

TP 347

0.08

2.00

0.045

0.030

0.75

9.0-13.0

17.0-19.0

-

 

Cb+TA10xC/10

 

SUMMARY OF THE MAIN ASTM STANDARDS GENERALLY USED FOR SHEETS / PLATES

ASTM

Grade

Chemical Requirements Percent (%)

Mechanical Requirements

C

max

Mn

Max

P

Max

S

Max

Si

Max

Ni

Cr.

Mo

Cu

Others

Tensile Strength

Mini-MPa(Ksi)

Yield Strength

Mini-MPa(Ksi)

Elong mini

%

Hardness

Brinell

Rockwell

A240

304

0.08

2.00

0.45

0.030

0.75

8.00-10.5

18.0-20.0

 

 

 

515-75

205-30

40

202

92

304L

0.030

2.00

0.45

0.030

0.75

8.00-12.0

18.0-20.0

 

 

 

485-70

170-25

40

183

88

310S

0.08

2.00

0.45

0.030

0.75

19.0-22.0

24.0-26.0

 

 

 

515-75

205-30

40

217

95

316

0.08

2.00

0.45

0.030

0.75

10.0-14.0

16.0-18.0

2.00-3.00

 

 

515-75

205-30

40

217

95

316L

0.030

2.00

0.45

0.030

0.75

10.0-14.0

16.0-18.0

2.00-3.00

 

 

485-70

170-25

40

217

95

317L

0.030

2.00

0.45

0.030

0.75

11.0-15.0

18.0-20.0

3.00-4.00

 

 

485-70

170-25

40

217

95

321

0.08

2.00

0.45

0.030

0.75

9.00-12.0

17.0-19.0

 

 

5(C+N) < Ti < 0.70%

515-75

205-30

40

217

95

347

0.08

2.00

0.45

0.030

0.75

9.00-13.0

17.0-19.0

 

 

10C < Cb+Ta < 1.10%

515-75

205-30

40

217

92

409

0.08

1.00

0.40

0.030

1.00

-

10.5-11.75

-

 

6 x C / 0.75 Ti max

448-65

241-35

25

183

75

A 387

Class 1

Class 2

 

 

 

 

 

 

 

 

 

 

 

Class 1

Class 2

Class 1

Class 2

 

 

 

2

0.05-0.021

0.55-0.80

0.035

0.040

0.15-0.40

 

0.50-0.80

0.45-0.60

 

 

380-550

486-620

230

310

22

Max201HB

Max92HRB

5

0.15

0.30-0.60

0.04

0.030

0.50

 

4.00-6.00

0.45-0.65

 

 

415-585

515-690

205

310

18

max202HB

Max92HRB

7

0.15

0.30-0.60

0.030

0.030

1.00

 

6.00-8.00

0.45-0.65

 

 

415-585

515-690

205

310

18

max217HB

Max95HRB

9

0.15

0.30-0.60

0.030

0.030

1.00

 

8.00-10.0

0.90-1.10

 

 

415-585

515-690

205

310

18

max217HB

Max95HRB

11

0.04-0.17

0.40-0.65

0.035

0.040

0.50-0.80

 

1.00-1.50

0.45-0.65

 

 

415-585

515-690

240

310

22

max217HB

Max95HRB

12

0.04-0.17

0.40-0.65

0.035

0.040

0.15-0.40

 

0.80-1.15

0.45-0.60

 

 

380-550

450-585

230

275

22

max217HB

Max95HRB

21

0.04-0.17

0.30-0.60

0.035

0.035

0.50

 

2.75-3.25

0.90-1.10

 

 

415-585

515-690

205

310

18

max201HB

Max92HRB

22

0.05-0.17

0.30-0.60

0.035

0.035

0.50

 

2.00-2.50

0.90-1.10

 

 

415-585

515-690

205

310

18

max201HB

Max92HRB

A515

55

0.22

0.90

0.035

0.04

0.15-0.40

 

 

 

 

 

380-515 / 55-75

205-30

27

 

60

0.27

0.90

0.035

0.04

0.15-0.40

 

 

 

 

 

415-550 / 60-80

220-32

25

 

65

0.31

0.90

0.035

0.04

0.15-0.40

 

 

 

 

 

450-585 / 65-85

240-35

23

 

70

0.33

1.20

0.035

0.04

0.15-0.40

 

 

 

 

 

485-620 / 70-90

260-38

21

 

A516

55

0.20

0.60-1.20

0.035

0.04

0.15-0.40

 

 

 

 

 

380-515 / 55-75

205-30

27

 

60

0.23

0.85-1.20

0.035

0.04

0.15-0.40

 

 

 

 

 

415-550 / 60-80

220-32

25

 

65

0.26

0.85-1.20

0.035

0.04

0.15-0.40

 

 

 

 

 

450-585 / 65-85

240-35

23

 

70

0.28

0.85-1.20

0.035

0.04

0.15-0.40

 

 

 

 

 

485-620 / 70-90

260-38

21

 

A537

Class 1

0.24

0.70-1.35

0.035

0.040

0.15-0.40

0.25 max

0.80 max

0.35 max

 

 

485-620 / 70-90

345-50

22

 

Class 2

0.24

0.70-1.35

0.035

0.040

0.15-0.40

0.25 max

0.80 max

0.35 max

 

 

550-690 / 80-100

415-60

22

 

 

IS-2062-92 STEEL FOR GENERAL STRUCTURAL PURPOSES

Grade

Designation

% Chemical Composition

Tensile

Strength

(Min)
Kg/mm2

Yield Strength (Min)

Mpa

%Elin gauge length 5.56 OSo

Bend Test

Std. test

Piece charpy

V Notch Impact

Energy Joule min

C

max

Mn

max

S

max

P

max

Si

max

C.E.

max

<20mm

20-40min

>40min

A

FE410WA

0.23

1.5

0.050

0.050

-

0.42

41.8

250

240

230

23

3T

-

B

FE410WB

0.22

1.5

0.045

0.045

0.40

0.41

41.8

250

250

230

23

2T-3T

2T for less than 25 mm

3T for more than 25 mm

C

FE410WC

0.20

1.5

0.040

0.040

0.40

0.39

41.8

250

250

230

23

2T

27

  

IS-2002-62 STEEL PLATES FOR BOILERS

                                                          Chemical Composition                                         Tensile-Test                                                                                                 Elongation

Designation

c

max

Si

max

P

max

S

max

Tensile Strength

Mpa

Yield Strength

Mpa

Test Piece

% min

IS 2002-1

0.18

0.10-0.35

0.040

0.040

362-442

540

5.65 ÖSo

4 ÖSo

26

30

IS 2002-2A

0.20

0.10-0.35

0.050

0.050

412-491

491

5.65 ÖSo

4 ÖSo

25

29

IS 2002-2B

0.22

0.10-0.35

0.050

0.050

510-608

491

5.65 ÖSo

4 ÖSo

20

24

  

ASTM A479 STAINLESS STEEL ROUND BAR CHEMICAL & PHYSICAL PROPERTIES

ASTM GRADE

C

Mn

Si

S

P

Cr

Ni

Mo

Other

Tensil

Psi(MPa)

Yield

Psi(MPa)

Elongation

Strip / Round

Hard-

ness

Redu. In Area. (%)

A479

TP 304

0.08

max

2.00

max

1.00

max

0.030

max.

0.045

max.

18.0

20.0

8.0

10.5

-

 

75000

(515)

30000

(205)

30

-

40

A479

TP 316

0.08

max

2.00

max

1.00

max

0.030

max.

0.045

max.

16.0

18.0

10.0

14.0

2.0

3.0

 

75000

(515)

30000

(250)

30

-

40

A479

TP 317L

0.035

max

2.00

max

1.00

max

0.030

max

0.045

max

18.0

20.0

11.0

15.0

3.0

4.0

 

75000

(515)

30000

(250)

30

-

40

A479

TP 310

0.08

max

2.00

max

1.00

max

0.030

max

0.045

max

24.0

26.0

19.0

22.0

 

-

75000

(515)

30000

(205)

30

-

40

A479

TP 347H

0.04

0.10

2.00

max

1.00

max

0.030

max

0.045

max

17.0

19.0

9.0

13.0

 

Cb-BxC

-13.0

75000

(515)

30000

(205)

30

-

40

479

TP 321

0.08

2.00

max

1.00

max

0.030

max

0.045

max

17.0

19.0

9.0

12.0

 

5(C+N)<Ti

<0.70%

75000

(515)

30000

(205)

30

-

40

 

ASTM A182 ALLOY STEEL ROUND BAR CHEMICAL & PHYSICAL PROPERTIES

ASTM GRADE

C

Mn

Si

S

P

Cr

Ni

Mo

Other

Tensil

Psi(MPa)

Yield

Psi(MPa)

Elongation

Strip / Round

Hard-

ness

Redu. In Area. (%)

182 F 11

Class 2

0.10

0.20

0.30

0.80

0.50

1.0

0.04

max

0.04

max

1.0

1.50

-

0.44

0.65

-

70000

(45.46)

40000

(27.05)

20

143-207

30

A 182 F22

Class 3

0.05

0.15

0.30

0.60

0.50

max

0.04

max

0.04

max

2.0

2.50

-

0.87

1.13.

-

75000

(52.52)

45000

(31.7)

20

156-207

30

A 182 F5

0.15

max

0.30

0.60

0.50

max

0.03

max

0.03

max

4.0

6.0

0.5

max

0.44

0.65

-

70000

(48.45)

40000

(27.05)

20

143-217

35

A 182 F9

0.15

max

0.30

0.60

0.50

1.00

0.03

max

0.03

max

8.0

10.0

-

0.90

1.10

-

85

(56.65)

55

(380)

20

179-217 (BHN)

40

 

IS-1875 ASTM A105 CARBON STEEL ROUND BAR CHEMICAL & PHYSICAL PROPERTIES

ASTM GRADE

C

Mn

Si

S

P

Cr

Ni

Mo

Other

Tensil

Psi(MPa)

Yield

Psi (MPa)

Elongation

Strip / Round

Hard-

ness

Redu. In Area. (%)

A 105

0.35

max

0.60

1.05

0.35

max

0.50

max

0.040

max

-

-

-

-

70000

(485)

36000

(250)

30-Strip

22-Round

187 max

30 Round

A LF2

0.30

max

1.35

max

0.15

0.30

0.040

max

0.035

max

0.30

max

0.40

max

0.12

max

Cu-0.4 max

Cb-0.02 max

Va-0.3 max

70-95

(485-655)

36

(250)

22 / 30

20 / 16

(-45.6o)

36